Red(HB) Color Glass Red glass Characteristic Type Thickness (mm) A[2856k] D65 Chemical Stability ND α×10-7 (℃) Tg (℃) Ts (℃) S x y Y x y Y DA DW HB600 2 0.680 0.319 27.0 0.675 0.325 16.5 1 2 1.523 103 527 605 2.64 HB610 2 0.695 0.305 18.4 0.690 0.310 10.7 1 2 1.523 103 527 605 2.64 HB630 2 0.713 0.287 10.4 0.711 0.289 5.5 1 2 1.523 103 527 605 2.64 HB640 2 0.724 0.276 5.0 0.723 0.277 2.4 1 2 1.523 103 527 605 2.64 HB650 2 0.728 0.272 3.2 0.728 0.272 1.5 1 2 1.523 103 527 605 2.64 HB670 2 0.731 0.269 1.1 0.730 0.270 0.5 1 2 1.523 103 527 605 2.64 HB685 2 0.734 0.266 0.3 0.734 0.266 0.1 1 2 1.523 103 527 605 2.64 HB700 2 0.735 0.265 0.0 0.735 0.265 0.0 1 2 1.523 111 534 592 2.64 Type Thk(mm) Cut on (nm) Range (nm) Trans (%) Bubble Stripe Stress HB600 2 600 ± 10 680-2500 ≥88.7 C-B 3C 3 HB610 2 610 ± 10 680-2500 ≥88.7 C-B 3C 3 HB630 2 630 ± 10 700-2500 ≥88.7 C-B 3C 3 HB640 2 640 ± 10 720-2500 ≥88.7 C-B 3C 3 HB650 2 650 ± 10 720-2500 ≥87.5 C-B 3C 3 HB670 2 670±10 750-2500 ≥87.5 C-B 3C 3 HB685 2 685±10 800-2500 ≥83.6 C-B 3C 3 HB700 2 700±10 800-2500 ≥79.8 C-B 3C 3 HB720 3 720±10 800-2500 ≥80.0 C-B 4 3
Red(HB) Color Glass
Red glass Characteristic Type Thickness (mm) A[2856k] D65 Chemical Stability ND α×10-7 (℃) Tg (℃) Ts (℃) S x y Y x y Y DA DW HB600 2 0.680 0.319 27.0 0.675 0.325 16.5 1 2 1.523 103 527 605 2.64 HB610 2 0.695 0.305 18.4 0.690 0.310 10.7 1 2 1.523 103 527 605 2.64 HB630 2 0.713 0.287 10.4 0.711 0.289 5.5 1 2 1.523 103 527 605 2.64 HB640 2 0.724 0.276 5.0 0.723 0.277 2.4 1 2 1.523 103 527 605 2.64 HB650 2 0.728 0.272 3.2 0.728 0.272 1.5 1 2 1.523 103 527 605 2.64 HB670 2 0.731 0.269 1.1 0.730 0.270 0.5 1 2 1.523 103 527 605 2.64 HB685 2 0.734 0.266 0.3 0.734 0.266 0.1 1 2 1.523 103 527 605 2.64 HB700 2 0.735 0.265 0.0 0.735 0.265 0.0 1 2 1.523 111 534 592 2.64
Red glass Characteristic
Type
Thickness (mm)
A[2856k]
D65
Chemical Stability
ND
α×10-7 (℃)
Tg (℃)
Ts (℃)
S
x
y
Y
DA
DW
HB600
2
0.680
0.319
27.0
0.675
0.325
16.5
1
1.523
103
527
605
2.64
HB610
0.695
0.305
18.4
0.690
0.310
10.7
HB630
0.713
0.287
10.4
0.711
0.289
5.5
HB640
0.724
0.276
5.0
0.723
0.277
2.4
HB650
0.728
0.272
3.2
1.5
HB670
0.731
0.269
1.1
0.730
0.270
0.5
HB685
0.734
0.266
0.3
0.1
HB700
0.735
0.265
0.0
111
534
592
Type Thk(mm) Cut on (nm) Range (nm) Trans (%) Bubble Stripe Stress HB600 2 600 ± 10 680-2500 ≥88.7 C-B 3C 3 HB610 2 610 ± 10 680-2500 ≥88.7 C-B 3C 3 HB630 2 630 ± 10 700-2500 ≥88.7 C-B 3C 3 HB640 2 640 ± 10 720-2500 ≥88.7 C-B 3C 3 HB650 2 650 ± 10 720-2500 ≥87.5 C-B 3C 3 HB670 2 670±10 750-2500 ≥87.5 C-B 3C 3 HB685 2 685±10 800-2500 ≥83.6 C-B 3C 3 HB700 2 700±10 800-2500 ≥79.8 C-B 3C 3 HB720 3 720±10 800-2500 ≥80.0 C-B 4 3
Thk(mm)
Cut on (nm)
Range (nm)
Trans (%)
Bubble
Stripe
Stress
600 ± 10
680-2500
≥88.7
C-B
3C
3
610 ± 10
630 ± 10
700-2500
640 ± 10
720-2500
650 ± 10
≥87.5
670±10
750-2500
685±10
800-2500
≥83.6
700±10
≥79.8
HB720
720±10
≥80.0
4